Product Details
Product Feature
The Copper Clad Wire has good corrosion resistance, which has longer service life for use and there is no special need of maintaining. In addition, it is completely covered with copper, and will not be contacted by water and air, and fully achieves the same performance as copper. The chloride ions contained in the salt spray in the atmosphere will condense on the surface of aluminum, which is easy to Impurities and defects around the surface cause local corrosion, forming holes, cracks, and microbatteries, thus to exacerbate the corrosion of aluminum conductors.
Product Description
The Copper Clad Wire is equipped with advanced process, which has longer service life for use. Due to the proper size and compact design, it can be placed everywhere in order to help release space of limited places. Compared with ordinary product on the market, it increases the total surface area of the conductor due to the increase in the total cross-section of the conductor, which improves the heat dissipation conditions of the cable and increases the heat dissipation area.
30% conductivity copper clad bare wire
Core diameter |
Copper layer thickness |
DC Resistance |
Nominal diameter |
Allowable error |
Minimum copper thickness |
Ω/km≦ |
1.67 |
+_0.015 |
0.072×2 |
≦27.0 |
1.628 |
+-0.015 |
0.070×2 |
≦28.5 |
1.45 |
+-0.015 |
0.062×2 |
≦36.2 |
1.29 |
+-0.0127 |
0.055×2 |
≦45.5 |
1.151 |
+-0.0127 |
0.049×2 |
≦57.2 |
1.024 |
+-0.01 |
0.044×2 |
≦72.5 |
0.813 |
+-0.0076 |
0.035×2 |
≦115 |
0.724 |
+-0.0076 |
0.031×2 |
≦145 |
0.643 |
+-0.0076 |
0.027×2 |
≦185 |
0.574 |
+-0.0076 |
0.024×2 |
≦232 |
1.511 |
+-0.0076 |
0.022×2 |
≦292 |
1.50 |
+-0.0076 |
0.017×2 |
≦473 |
tensile strength Hard state is not less than 827Mpa Soft state is not less than 380Mpa |
Elongation Hard state is not less than 8% |